Invar 32 Rod UNS-K-93500
Super-Invar32-5 Rod
Consisting of 32% Nickel, 5% Cobalt, and the balance Iron, this alloy exhibits minimum thermal expansion (one half of Invar 36) at room temperature. It is often used in structural components, supports and substrates requiring precision measurements
Applications
Optical and laser systems
Telescopes
Laser bench tops
Ring laser gyroscopes
Main features:
Low expansion coefficient in the range of 20-100 ° C
Russia
|
USA
|
England
|
Japan
|
Franch
|
--
|
Super-Invar32-5
|
SI
|
Invar
|
---
|
Content Composition %
C
|
Si
|
P
|
S
|
Cu
|
Mn
|
Co
|
|
Ni
|
Fe
|
Less than% (≤)
|
|
0.05
|
0.20
|
0.020
|
0.020
|
0.4-0.8
|
0.2-0.6
|
3.2-4.2
|
|
31.5-33.0
|
Rest
|
Average linear expansion coefficient
Sample heat treatment system
|
ā/(10-6/℃)
|
20-100℃
|
20-300℃
|
The semi-finished sample is heated to 840±10° C., kept for 1 h, water quenched, and then the sample is processed into a finished sample, which is kept at 315 ° C ± 10 ° C for 1 h with furnace cooling or air cooling.
|
≤1.0
|
...
|
Line thermal expansion
20-50℃
|
20-100℃
|
20-200℃
|
20-300℃
|
20-400℃
|
20-500℃
|
0.7
|
0.8
|
1.4
|
4.3
|
7.2
|
9.3
|
Type
|
Size/mm
|
Deliver State
|
Bar
|
5.0-8.0
|
Cold Drawn
|
8.0-30.0
|
Hot rolling
|
30.0-180.0
|
Hot forging
|
Plate
|
3.5-30.0
|
Hot rolling
|
30.0-40.0
|
Hot forging
|
Strip
|
0.2-3.5
|
Cold rolling
|
Flat wire
|
0.5-5.0
|
Hot rolling
|
Round wire
|
0.1-5.0
|
Cold Drawn
|
Capillary
|
OD8.0-1.0,ID0.1-8.0
|
Cold Drawn
|
Pipe
|
OD120-8.0, ID8.0-129
|
Cold drawn
|