Tungsten alloy bar is produced by pressing and sintering metal powders into billets, which are worked by rolling or swaging into rod. Smaller sizes are produced by subsequent drawing. Tungsten alloy rod is produced in straight random lengths with a smooth swaged surface at diameters 3mm and larger, and with a smooth drawn finish below 3mm. A centerless ground finish can also be furnished. Specific lengths and special fabrications can be supplied upon request.
Tungsten Alloy bar Specifications
1, Diameter: 2.0-100.0mm (according customer required)
2, Length: 50-1000mm
3, Density: 15.8-18.75 g/cm3
4, Composition: W content: 85-99%, W-Ni-Fe, W-Ni-Cu
5, Surface: Sintering surface, Forged surface, Ground surface
|
HD 17 |
HD 17BB |
HD 17D |
HD 17.5 |
HD17.7 |
HD 18 |
HD 18D |
HD 18.5 |
90%W
6% Ni
4% Cu |
90% W
6% Ni
4%Cu/Fe |
90% W
7% Ni
3% Fe |
92.5% W
5.25%Ni
2.25%Fe |
93WBalanceNi FeMo |
95% W
3.5%Ni
1.5%Cu |
95% W
3.5% Ni
1.5% Fe |
97% W
2.1% Ni
9% Fe |
Density Gms/cc |
17 |
17 |
17.5 |
17.7 |
18 |
18 |
18.5 |
Hardness Rockwell |
24 |
25 |
26 |
30 |
27 |
27 |
28 |
Ultimate Tensile Strength (PSI) |
110,000 |
125,000 |
114,000 |
130,000 |
115,000 |
125,000 |
128,000 |
Yield Strength .2% offset (PSI) |
90,000 |
88,000 |
90,000 |
90,000 |
85,000 |
90,000 |
85,000 |
Elongation (% in 1") |
8 |
14 |
12 |
10 |
7 |
12 |
10 |
Coefficient of Thermal Expansion X 10-6/°C (20-400°C) |
5.4 |
4.8 |
4.6 |
4.5 |
4.4 |
4.6 |
4.5 |
Thermal Conductivity (CGS Units) |
.23 |
.18 |
.20 |
27 |
.33 |
.26 |
.30 |
Electrical Conductivity
(% IACS) |
14 |
10 |
13 |
14 |
16 |
13 |
17 |
Magnetic Properties |
HD 17 = NIL
HD 17BB = Slightly Magnetic |
Slightly
Magnetic |
Slightly
Magnetic |
Slightly
Magnetic |
NIL |
Slightly
Magnetic |
Slightly
Magnetic |
Product specifications:1 ball: φ≥ 1.5mm
2 long and thin rod: (φ≥1mm)×(L≤600mm)